CsPbBr<sub>3</sub>-based photoanode prepared by single-step Chemical vapor deposition of tunable thickness perovskite films

Simple item page
dc.contributor.authorSosa-Acosta, J. R.
dc.contributor.authorFernandez-Izquierdo, L.
dc.contributor.authordel Rio, Rodrigo
dc.contributor.authorNavarrete-Astorga, Elena
dc.contributor.authorLeinen, Dietmar
dc.contributor.authorHevia, Samuel A.
dc.date.accessioned2025-01-20T16:07:59Z
dc.date.available2025-01-20T16:07:59Z
dc.date.issued2024
dc.description.abstractCesium Lead Bromide (CsPbBr3) perovskite films have gained significant attention in photoelectrochemistry due to their promising properties. However, their widespread application necessitates scalable processing methods to produce high-quality films. Current techniques often involve post-synthesis steps to achieve desirable crystalline films or surface coverage for optimal performance. This research performed a single-step Chemical Vapor Deposition (CVD) approach to grow high-quality CsPbBr3 films. This methodology offers precise control over film thickness and grain orientation, crucial for optimizing photoelectrochemical response. The procedure simplifies fabrication by bypassing annealing or toxic solvent excess and growing films directly from CsPbBr3 crystals. Film thickness was controlled by adjusting growth time and precursor mass parameters to examine the photoelectrochemical performance across thicknesses ranging from 0.6 mu m to 2.5 mu m. Optimal results were achieved with dense, compact films 1.5 mu m thick, which exhibited oriented grains along the (121) plane. Optical, structural, and morphological analyses confirmed a predominantly pure orthorhombic phase, although slight impurities were noted in thinner films. The 1.5 mu m films showed a four-hour stable photocurrent of 6.2 mA/cm2 at 1.23 V versus reversible hydrogen electrode (RHE) under simulated solar conditions, underscoring their potential in advancing perovskite-based electrodes for efficient photoelectrochemical solar fuel generation.
dc.fuente.origenWOS
dc.identifier.doi10.1016/j.apsusc.2024.161049
dc.identifier.eissn1873-5584
dc.identifier.issn0169-4332
dc.identifier.urihttps://doi.org/10.1016/j.apsusc.2024.161049
dc.identifier.urihttps://repositorio.uc.cl/handle/11534/90040
dc.identifier.wosidWOS:001321993700001
dc.language.isoen
dc.revistaApplied surface science
dc.rightsacceso restringido
dc.subjectPerovskite
dc.subjectSingle-step chemical vapor deposition
dc.subjectPhotoanode
dc.subjectWater splitting
dc.subject.ods07 Affordable and Clean Energy
dc.subject.odspa07 Energía asequible y no contaminante
dc.titleCsPbBr<sub>3</sub>-based photoanode prepared by single-step Chemical vapor deposition of tunable thickness perovskite films
dc.typeartículo
dc.volumen678
sipa.indexWOS
sipa.trazabilidadWOS;2025-01-12
Files
Collections
Artículos de revistas